The Five Most Common Aluminum Plate
5083 Aluminum Plate
Haomei en aw 5083 h321 has been widely used for C80 coal truck, liquid tankers, refrigerated trucks, new energy passenger cars,etc. 5083 belongs to the heat-treated alloy that has good workability, corrosion resistance and welding performance. We also realize the mass production of 5083/5454/5182-H111 (5-8mm×1800-2400mm×5000-12000mm)by hot continuous rolling, which has won unanimous praise from users.
1060 Aluminum Sheet
It belongs to pure aluminium alloy. The production process is relatively simple and the technology is relatively complete, which has huge price advantage. It has excellent tensile strength and compressive strength.
1060 aluminum chemical composition: iron (Fe) 0.35%, manganese (Mn) 0.03%, magnesium (Mg) 0.03%, silicon (Si) 0.25%, zinc (Zn) 0.05%, titanium (Ti) 0.03%, copper (Cu) 0.05 %. Aluminum (Al) exceeds 99.6%.
Mechanical properties: 1060 aluminum plate’s compressive strength is higher than 75 MPa, and compromise strength is higher than 35 MPa.
3003 Aluminum Plate
3003 aluminum plate is a representative product of the aluminum-manganese alloy, featuring excellent anti-rust performance.
3003 chemical composition: Al: remainder; Si: 0.6, Cu: 0.05--0.2, Zn: 0.10, Mn: 1.0--1.5, Fe: 0.7, each of the rest alloy element: 0.05.
Mechanical properties: tensile strength σb (MPa)) 120-160
7075 Aluminum Plate
7075 sheet mechanical properties: tensile strength: 524Mpa, 0.2% yield strength: 455Mpa, elastic modulus E: 71GPa, hardness: 150HB, density: 2.81g/cm3.
Chemical composition: Si: 0.40, Fe: 0.50, Cu: 1.2-2.0, Mn: 0.30, Mg: 2.1-2.9, Cr: 0.18-0.28, Zn: 5.1-6.1, Ti: 0.20 ,each of the rest alloy element: 0.05, Al: remainder.
6061 Aluminum Sheet
6061 aluminum is a high-quality aluminum alloy product manufactured by the heat treatment process and pre-stretching process. Although its strength cannot be compared with the 5XXX series or 7XXX series, it has excellent corrosion resistance, high ductility and good anodizing effect.